Pengaruh Temperatur Pengeringan Gel terhadap Konduktivitas Elektrolit Padat NaMn2-xMgxO4 Feni Risyanti; Rahmad Nuryanto; Linda Suyati
Jurnal Kimia Sains dan Aplikasi Vol 15, No 2 (2012): Volume 15 Issue 2 Year 2012
Publisher : Chemistry Department, Faculty of Sciences and Mathematics, Diponegoro University

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (414.8 KB) | DOI: 10.14710/jksa.15.2.44-46

Abstract

Pembuatan elektrolit padat NaMn2-xMgxO4 dengan variasi temperatur pengeringan telah dilakukan. Tujuan penelitian ini adalah untuk mengetahui pengaruh variasi temperatur pengeringan gel terhadap konduktivitas elektrolit padat NaMn2-xMgxO4. Metode yang digunakan dalam penelitian yang dilakukan adalah metode sol-gel yang meliputi pengadukan, penguapan pada 80°C, pengeringan pada variasi temperatur 150, 160, 170, 180 dan 190°C, dan kalsinasi pada 800°C. Produk yang dihasilkan dianalisis dengan uji konduktivitas, FTIR dan XRD. Hasil pengukuran konduktivitas padatan amorf dan elektrolit padat berdasarkan variasi temperatur pengeringan menunjukkan nilai konduktivitas tertinggi diperoleh pada temperatur 170°C yaitu masing-masing 2,27 x 10-9 S cm-1 dan 22,2 x 10-9 S cm-1. Konduktivitas terendah untuk padatan amorf dan elektrolit padat diperoleh pada temperatur 150°C yaitu masing-masing sebesar 1,87 x 10-9 S cm-1 dan 12,6 x 10-9 S cm-1.