<![CDATA[Nanocellulose is widely applied in various fields due to its superior characteristics. Several methods have been developed to synthesize it, but they still have limitedness as being non-eco-friendly and inefficient use. Therefore, the synthesis of nanocellulose from sustainable sources is being developed using a simple and eco-friendly method. This study successfully produced a low viscosity gel suspension of cellulose nanofibers (CNF) from bacterial cellulose (BC) derived from Nata de Coco using a high shear mixer (HSM). The mixture of BC and water in a 1:1 ratio was processed with various rotational speeds and times in the HSM. The suspension result was characterized using an Ostwald viscometer, UV-vis spectrophotometer, lux meter, scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), particle size analyzer (PSA), and x-ray diffraction (XRD). Based on the characterization, it was confirmed that higher rotational speeds and extended processing times reduced the suspension viscosity and increased light transmittance, indicating a reduction in BC size to the submicron/nanometer scale. The best light transmittance was achieved with the HSM at 4500 rpm for 180 min, resulting in a viscosity drop from 232.67 mPa.s to 1.45 mPa.s. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) analysis showed that the CNF retained its fibrous structure with nanometer-scale widths and high porosity without significant changes in crystallinity.]]>