Article Per Year (5 Year)
p-Index From 2020 - 2025
0.408
P-Index
This Author published in this journals
All Journal Jurnal Kumparan Fisika Newton-Maxwell Journal of Physics
Susanto, Yuris
Unknown Affiliation
Astronomy Earth & Planetary Sciences Education Electrical & Electronics Engineering Mechanical Engineering Physics

Published : 2 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 2 Documents
Search

 1 
Identifikasi Limbah Cair Kelapa Sawit di Desa Tinting Boyok Kabupaten Sekadau Provinsi Kalimantan Barat Berdasarkan Nilai Resistivitas Zulfian, Zulfian; Susanto, Yuris
Jurnal Kumparan Fisika Vol. 8 No. 1: April 2025 : IN PRESS
Publisher : Unib Press

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.33369/jkf.8.1.1-10

Abstract

ABSTRAK   Limbah cair kelapa sawit telah diterapkan di lahan aplikasi yang berada di Desa Tinting Boyok, Kabupaten Sekadau, Provinsi Kalimantan Barat. Tujuan penelitian ini adalah untuk mengidentifikasi limbah cair kelapa sawit yang merembes ke dalam tanah. Rembesan limbah ini dikhawatirkan menurunkan kualitas air tanah. Metode yang digunakan untuk mencapai tujuan tersebut adalah metode geolistrik resistivitas dengan konfigurasi Wenner-Schlumberger. Penelitian ini menggunakan dua lintasan geolistrik dengan panjang lintasan sebesar 195 m. Identifikasi limbah cair kelapa sawit dilakukan berdasarkan nilai resistivitas yang diperoleh dari proses pemodelan menggunakan metode inversi Gauss-Newton. Dari proses inversi tersebut, penampang resistivitas yang diperoleh dapat menyatakan nilai resistivitas sebenarnya. Nilai resistivitas yang diperoleh dari hasil inversi adalah 4,53 Ωm  s.d. 950 Ωm. Dari nilai resistivitas tersebut, lapisan tanah yang terdapat pada daerah penelitian berupa lapisan pasir, pasir lempungan dan lapukan granodiorit. Lapisan pasir diduga sebagai tempat akumulasi limbah cair kelapa sawit di dalam tanah. Limbah cair kelapa sawit diduga memiliki nilai resistivitas 4,53 Ωm s.d. 9,7 Ωm. Limbah cair kelapa sawit memiliki nilai resistivitas yang lebih kecil karena mengandung Chemical Oxigen Demand (COD) dan Biochemical Oxygen Demand (BOD) tinggi serta logam hingga logam berat. Rembesan limbah ini diduga terdeteksi dari kedalaman 2 m s.d. 6,5 m pada lintasan 1 dan 2 m s.d. 24 m. Formasi geologi dan topografi mempengaruhi rembesan limbah pada lintasan 1 dan lintasan 2.   Kata  kunci— metode geolistrik, limbah cair kelapa sawit, resistivitas   ABSTRACT   Palm oil mill effluent (POME) has been applied to the application site located in Tinting Boyok Village, Sekadau Regency, West Kalimantan Province. The objective of this research is to identify the seepage of palm oil mill effluent into the soil. This seepage is concerning as it may degrade the quality of groundwater. The method used to achieve this objective is the resistivity geoelectric method with the Wenner-Schlumberger configuration. This study utilized two geoelectric lines, each with a length of 195 meters. The identification of palm oil mill effluent was based on resistivity values obtained from the modeling process using the Gauss-Newton inversion method. From this inversion process, the resistivity cross-section obtained can represent the actual resistivity values. The resistivity values obtained from the inversion results range from 4.53 Ωm to 950 Ωm. Based on these resistivity values, the soil layers in the study area consist of sand, clayey sand, and weathered granodiorite layers. The sand layer is suspected to be the accumulation zone for palm oil mill effluent within the soil. The palm oil mill effluent is estimated to have resistivity values ranging from 4.53 Ωm to 9.7 Ωm. The effluent exhibits lower resistivity values due to its high Chemical Oxygen Demand (COD) and Biochemical Oxygen Demand (BOD) content, as well as the presence of metals and heavy metals. The seepage of this effluent is suspected to be detected at depths ranging from 2 meters to 6.5 meters on line 1, and from 2 meters to 24 meters on line 2. Geological formations and topography influence the seepage of the effluent on both line 1 and line 2..   Keywords— geoelectrical method, palm oil mill efflunet, resistivity
Karakteristik Sifat Kimia, Fisis, dan Mekanik Papan Komposit Berbahan Baku Limbah Tulang Daun Kratom Anderesta, Fani Chelsea; Susanto, Yuris; Nurhanisa, Mega
Newton-Maxwell Journal of Physics Vol. 6 No. 1: April 2025
Publisher : UNIB Press

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.33369/nmj.v6i1.37073

Abstract

Penelitian ini mengkaji potensi limbah tulang daun kratom (Mitragyna speciosa) sebagai bahan pengisi (filler) dalam pembuatan papan komposit. Fokus kajian meliputi evaluasi karakteristik sifat kimia bahan baku serta sifat fisis dan mekanik dari papan komposit yang dihasilkan. Hasil analisis kimia menunjukkan bahwa tulang daun kratom mengandung lignin sebesar 16,83%, holoselulosa 59,65%, α-selulosa 38,60%, hemiselulosa 21,05%, dan zat ekstraktif sebesar 26,39%, yang mengklasifikasikan bahan ini sebagai sumber lignoselulosa dengan kadar lignin rendah dan hemiselulosa sedang. Papan komposit diproduksi menggunakan resin urea-formaldehida sebanyak 16%, kemudian dikempa panas pada suhu 200°C dengan tekanan 25 Pa selama 10 menit. Papan yang dihasilkan memiliki kerapatan sebesar 0,55 g/cm³, kadar air 3,89%, pengembangan tebal 57,07%, keteguhan tarik 0,83 kgf/cm², modulus patah (MOR) sebesar 70,91 kgf/cm², dan modulus elastisitas (MOE) sebesar 9.057,6 kgf/cm². Seluruh parameter memenuhi standar SNI 01-4449-2006, kecuali untuk pengembangan tebal. Hasil pengujian ini menunjukkan bahwa, meskipun kandungan zat ekstraktif yang tinggi dan sifat higroskopisnya menyebabkan ketidakstabilan dimensi, limbah tulang daun kratom tetap memiliki karakteristik yang menjanjikan sebagai bahan baku papan komposit berkelanjutan apabila diberikan perlakuan yang tepat.
Co-Authors Anderesta, Fani Chelsea Mega Nurhanisa Zulfian Zulfian