PENGARUH PEMAKAIAN AGREGAT HALUS (MUNTILAN, KALI BODRI, SINGOROJO) TERHADAP KUAT TEKAN BETON PADA VARIASI GEOMETRI SILINDER Abidin, Ali Nur; Panolas, Yoga Bagus; Budirahardjo, Slamet; Kristiawan, Agung
Jurnal Teknik Sipil Giratory UPGRIS Vol 3, No 1: Juni 2022
Publisher : Universitas PGRI Semarang

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.26877/giratory.v3i1.12849

Abstract

Penggunaan beton semakin meningkat seiring dengan perkembangan zaman. Penggunaan beton sebagai salah satu pilihan disebabkan karena beton memiliki sifat kuat tekan yang tinggi. Core drill adalah suatu metode pengambilan sampel beton pada suatu struktur bangunan. Sampel yang diambil (bentuk silinder) selanjutnya dibawa ke laboratorium untuk dilakukan pengujian seperti kuat tekan. Penelitian ini bertujuan untuk menganalisis kuat tekan beton dengan perbandingan 1PC:2PS:3KR pada ukuran silinder 15 x 30 cm, dan perbandingan 1PC:2PS:3KR pada ukuran silinder 10 x 15 cm, 10 x 18 cm, 10 x 20 cm, dengan agregat halus (muntilan, kali bodri, dan singorojo). Penelitian ini menggunakan pendekatan kuantitatif dengan eksperimen. Sampel penelitian ini menggunakan beton keras dengan mengganti agregat halus pasir muntilan, kali bodri, dan singorojo. Pengujian menunjukan nilai kuat tekan beton dengan perbandingan 1PC:2PS:3KR dengan ukuran silinder 15 x 30cm dengan agregat halus umur 14 hari nilai kuat tekan beton (muntilan : 10,19 Mpa, kali bodri ; 8,90 Mpa, singorojo : 8,90 Mpa) dan umur 21 hari (muntilan : 11,22 Mpa, kali bodri : 9,73 Mpa, singorojo : 9,34 Mpa). Pengujian menggunakan cetakan variasi geometri silinder (10 x 20cm, 10 x 18cm, 10 x 15cm) mempengaruhi nilai kuat beton dan pemakaian agregat halus yang berbeda (pasir muntilan, kali bodri, dan singorojo) juga mempengaruhi nilai kuat tekan beton. Dari hasil perbandigan 1PC:2PS:3KR penggunaan pasir muntilan lebih disarankan untuk material kontruksi beton karena nilai kuat tekan beton pasir muntilan lebih tinggi.Kata Kunci: Pasir Muntilan, Kali Bodri, Singorojo, Kuat Tekan
PENGARUH PEMAKAIAN AGREGAT HALUS (MUNTILAN, KALI BODRI, SINGOROJO) TERHADAP KUAT TEKAN BETON PADA VARIASI GEOMETRI SILINDER Abidin, Ali Nur; Panolas, Yoga Bagus; Budirahardjo, Slamet; Kristiawan, Agung
Jurnal Teknik Sipil Giratory UPGRIS Vol 3, No 1: Juni 2022
Publisher : Universitas PGRI Semarang

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.26877/giratory.v3i1.12849

Abstract

The use of concrete is increasing along with the times. The use of concrete as an option is due to the fact that concrete has high compressive strength properties. Core drill is a method of taking concrete samples in a building structure. The sample taken (cylindrical shape) is then taken to the laboratory for testing such as compressive strength. This study aims to analyze the compressive strength of concrete with a ratio of 1PC:2PS:3KR on a cylinder size of 15 x 30 cm, and a ratio of 1PC:2PS:3KR on a cylinder size of 10 x 15 cm, 10 x 18 cm, 10 x 20 cm, with fine aggregate (muntilan, kali bodri, and singgorojo). This study uses a quantitative approach with experiments. The sample of this study used hard concrete by replacing the fine aggregate of muntilan sand, Kali Bodri, and Singgorojo. The test shows the value of the compressive strength of concrete with a ratio of 1PC:2PS:3KR with a cylinder size of 15 x 30cm with fine aggregate aged 14 days, the value of the compressive strength of concrete (muntilan: 10.19 Mpa, times bodri; 8.90 Mpa, singorojo: 8 ,90 Mpa) and 21 days old (muntilan : 11.22 Mpa, Kali Bodri : 9.73 Mpa, Singgorojo : 9.34 Mpa). Tests using cylindrical geometry variations (10 x 20cm, 10 x 18cm, 10 x 15cm) affect the value of concrete strength and the use of different fine aggregates (muntilan sand, Kali Bodri, and Singgorojo) also affects the value of the compressive strength of concrete. From the results of the comparison 1PC:2PS:3KR the use of muntilan sand is more recommended for concrete construction materials because the compressive strength of muntilan sand concrete is higher.
Co-Authors Agung Kristiawan Panolas, Yoga Bagus Slamet Budirahardjo