KARAKTERISASI SIFAT FISIS DAN MEKANIS PENGELASAN ALUMINIUM SERI AA-5052 DENGAN METODE FRICTION STIR WELDING, DENGAN FEED RATE 60 MM/MENIT PADA PUTARAN 1500 RPM DAN SUDUT KEMIRINGAN TOOLS 30 YANG DILANJUTKAN ANNEALING DAN NORMALIZING

BIbit Sugito (Universitas Muhammadiyah Surakarta)
Pramuko Ilmu Purbo Putro (Department of Mechanical Engineering, Faculty of Engineering, Universitas Muhammadiyah Surakarta)
Agus Dwi Anggono (Department of Mechanical Engineering, Faculty of Engineering, Universitas Muhammadiyah Surakarta)
Agung Setyo Darmawan (Department of Mechanical Engineering, Faculty of Engineering, Universitas Muhammadiyah Surakarta)
Masyrukan Masyrukan (Department of Mechanical Engineering, Faculty of Engineering, Universitas Muhammadiyah Surakarta)
Aditya Qomarudin (Department of Mechanical Engineering, Faculty of Engineering, Universitas Muhammadiyah Surakarta)

Media Mesin: Majalah Teknik Mesin
Vol 23, No 1 (2022)

Tujuan penelitian ini untuk mengetahui pengaruh annealing dan normalizing dari  pengelasan aluminium seri AA 5052 terhadap struktur mikro, tegangan tarik, dan kekerasan. Proses pengelasan dengan parameter feed rate 60 mm/menit, kemiringan tools 3º,  kecepatan putar 1500 rpm. Hasil penelitian didapatkan kekuatan tarik raw material sebesar 162.54 MPa dengan regangan sebesar 8.61%, kekuatan tarik yang di annealing dan normalizing masing-masing 157.86 Mpa dengan regangan 7.41%, dan 141.66 Mpa dengan regangan 8.18 %. Sedangkan nilai kekerasan pada base metal sebesar 53.7 BHN, daerah HAZ 40.6 BHN, daerah lasan 30.4 BHN. Nilai kekerasan yang di annealing dan normalizing masing – masing sebesar 23.6 BHN pada raw material, HAZ 23.6 BHN daerah lasan 20.2  BHN, sedangkan yang normalizing 26.1 BHN, HAZ 22.7 BHN dan daerah lasan 21.6 BHN. Pada pengamatan struktur mikro perlakuan panas annealing dan normalizing mengalami penghalusan butir yang dapat dilihat pada foto terlihat mengecil dan merapat.