Studi Eksperimen Variasi Paduan Al-Si pada Rangka Urban Diesel KMHE

Wilujeng, Auliana Diah
Suwanto, Eko
Annafiyah, Annafiyah
Abdi, Ferly Isnomo

Jurnal Rekayasa Mesin
Vol 9 No 01 (2024): JRM April 2024

Abstrak: Chassis merupakan komponen terpenting yang berfungsi untuk menompang berat kendaraan, mesin, penompang, serta menahan agar kendaraan tetap dalam stabil dan tidak mengalami defleksi berlebih. Besarnya kebutuhan pasar yang menginginkan bahan chassis yang ringan dan kuat, sehingga banyak yang melakukan inovasi-inovasi tentang pembuatan material chassis yang cocok digunakan dalam kendaraan dengan melakukan penelitian tentang paduan beberapa material logam. Pada penelitian ini, chassis dibuat dengan material Aluminium (Al) yang dipadukan dengan Silika (Si) melalui proses pengecoran. Dari hasil perpaduan tersebut, dilakukan prngujian tensile test dan bending test. Aluminium dileburkan pada titik leburnya serta ditambahkan serbuk Si dengan komposisi 0%, 2%, 4%, dan 6% kemudian dilakukan pencetakan sesuai standar material uji. Hasil yang diperoleh dari pengujian adalah Silika dapat mengubah sifa mekanis dari Alumunium. Pada pengujian tekuk, semakin besar persentase Si maka semakin rendah peak loadnya. Sedangkan pada pengujian tarik, peak load semakin besar seiring bertambahnya persentase Si. Kata kunci: Silika, Alumunium, Paduan, Chassis, KMHE. Abstract: The chassis is the most important component which functions to support the weight of the vehicle, engine, passengers, and to keep the vehicle stable and not experience excessive deflection. The large market demand for chassis materials that are light and strong means that many are making innovations regarding the manufacture of chassis materials that are suitable for use in vehicles by conducting research on alloys of several metal materials. In this research, the chassis was made from Aluminum (Al) material combined with Silica (Si) through a casting process. From the results of this combination, tensile tests and bending tests were carried out. Aluminum is melted at its melting point and Si powder is added with a composition of 0%, 2%, 4% and 6%, then molding is carried out according to the test material standards. The results obtained from the test are that Silica can change the mechanical properties of Aluminum. In the bending test, the greater the Si percentage, the lower the peak load. Meanwhile, in the tensile test, the peak load increases as the Si percentage increases. Keywords: Silica, Aluminum, Alloy, Chassis, KMHE.