<![CDATA[AbstractConcrete is one of the most widely used construction materials owing to its excellent compressive strength. Nevertheless, its long-term performance remains susceptible to environmental factors. Fluctuations in temperature, humidity, and solar radiation can significantly impair concrete durability and structural integrity. This study explores the potential of utilizing sawdust waste as a partial replacement (2% by weight of fine aggregate) to improve environmental sustainability while evaluating its effects on mechanical properties. The research investigates the compressive strength of concrete incorporating 2% sawdust at curing ages of 28, 45, and 60 days under two distinct exposure conditions: indoor (controlled) and outdoor (natural) environments. An experimental laboratory approach was adopted using the Department of the Environment (DoE) mix design method. Cube specimens (150 × 150 × 150 mm) were prepared in two variants: normal concrete and concrete with 2% sawdust substitution. Results reveal that the incorporation of sawdust reduces compressive strength compared to control specimens, although strength continues to increase with curing age in both groups. Specimens cured indoors exhibited more consistent strength gain, whereas those exposed outdoors experienced a noticeable strength decline at 60 days. While the use of sawdust as a partial fine aggregate replacement offers an environmentally sound waste valorization strategy, it adversely affects mechanical performance and long-term durability. Further research is recommended prior to its practical implementation in structural applications.Keywords:Concrete; sawdust; compressive strengthAbstrakBeton merupakan material konstruksi yang paling banyak digunakan karena memiliki kuat tekan tinggi. Namun, beton tetap rentan terhadap pengaruh lingkungan dalam jangka panjang. Variasi suhu, kelembaban, dan radiasi matahari dapat menurunkan durabilitas serta kinerja struktural beton secara signifikan. Penelitian ini bertujuan untuk mengevaluasi pengaruh substitusi agregat halus dengan limbah serbuk gergaji sebesar 2 % (berdasarkan berat pasir) terhadap kuat tekan beton pada umur 28, 45, dan 60 hari, serta menganalisis pengaruh kondisi paparan lingkungan yang berbeda (dalam ruangan dan luar ruangan) terhadap perkembangan kuat tekan tersebut. Metode penelitian yang digunakan adalah eksperimen laboratorium dengan desain campuran berdasarkan pendekatan Department of the Environment (DoE). Spesimen berbentuk kubus berukuran 150 × 150 × 150 mm dibuat dalam dua variasi, yaitu beton normal (kontrol) dan beton dengan substitusi serbuk gergaji 2 %. Hasil pengujian menunjukkan bahwa penambahan serbuk gergaji menyebabkan penurunan kuat tekan dibandingkan beton kontrol, meskipun kuat tekan kedua variasi tetap meningkat seiring bertambahnya umur perawatan. Spesimen yang disimpan di dalam ruangan menunjukkan perkembangan kuat tekan yang lebih stabil, sedangkan spesimen yang dipaparkan di luar ruangan mengalami penurunan kuat tekan pada umur 60 hari. Penggunaan serbuk gergaji sebagai pengganti sebagian agregat halus memberikan manfaat lingkungan melalui pemanfaatan limbah, tetapi berpotensi menurunkan kinerja mekanis dan durabilitas beton dalam jangka panjang. Oleh karena itu, diperlukan penelitian lebih lanjut sebelum material ini dapat direkomendasikan untuk aplikasi struktural secara luas. Kata Kunci:Beton; serbuk kayu; kuat tekan]]>
Copyrights © 2025
