Pengaruh media pendingin dan waktu pada perlakuan pack carburizing-quenching baja karbon rendah SS400 Sujita, S.; Yudhyadi, I.G.N.K.; Zainuri, A.; Adhi, I.G.A.K.C.; Sutanto, R.
Dinamika Teknik Mesin: Jurnal Keilmuan dan Terapan Teknik Mesin Vol 11, No 2 (2021): Dinamika Teknik Mesin: Jurnal Keilmuan dan Terapan Teknik Mesin
Publisher : Universitas Mataram

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (517.339 KB) | DOI: 10.29303/dtm.v11i2.471

Abstract

The SS400 low carbon steel is widely used in the agricultural equipment industry because of its specific properties, malleability good corrosion resistance, and high strength to weight ratio. However, according to several research results it has several weaknesses, low surface hardness, ductility and wear resistance. Therefore, it is necessary to improve its mechanical properties so that the agricultural equipment products produced are of better quality. The purpose of this study was to determine the effect of variations in time and cooling media in the pack carburizing-quenching treatment of SS400 steel specimens. The pack carburizing treatment was carried out at a temperature of 875 ºC, 90 minutes, the carburizing medium was a mixture of corncob charcoal powder and Picntada maxima shell powder, with a composition of 70%: 30%, followed by a quenching process with variations in time (1, 2, 3, 4). minutes) and cooling medium (water, oil SAE 40, cane molasses 10% and  cane molasses 30%. The results of the study showed that the time and cooling medium affected the surface hardness, ductility and microstructure of the specimens With 30% cane molasses cooling medium, quenching time of 4 minutes, the largest specimen absorbed impact energy (toughness) is 2.23 J/mm2. On the other hand, the lowest surface hardness number is 285 Kg/mm2.The increased ductility causes the cracking marks to disappear on the specimen surface. Based on observations with SEM, there is a decomposition of the martensite structure with coarser grain sizes. 
Studi eksperimental terhadap porositas dan hambat alir udara pada komposit penyerap suara Sari, N.H.; Fajrin, J.; Yudhyadi, I.G.N.K.
Dinamika Teknik Mesin: Jurnal Keilmuan dan Terapan Teknik Mesin Vol 8, No 1 (2018): Dinamika Teknik Mesin: Jurnal Keilmuan dan Terapan Teknik Mesin
Publisher : Universitas Mataram

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (987.506 KB) | DOI: 10.29303/dtm.v8i1.100

Abstract

In this paper, we present a comprehensive analytical and experimental investigation for the determination of the air flow resistivity and porosity of sound absorber composite. The ratio of the volume fraction of fiber and polyester resin is 15, 25, 35, 55 and 65 (%).The dimensions of the absorbent composite sample are 29 mm x 20 cm (diameter x thickness). Porosity and Air flow resistivity of composites have been investigated. The results showed that the porosity of the composites increased with increasing amount of fiber due to the interface between fiber and resinless dense. In contrast, the air flow resistivity values are lower with a denser resin and fiber interface.
Efek suhu sintering terhadap sifat kekerasan bahan campuran Al/Cu/Sic melalui proses metalurgi serbuk Triadi, A.A.A.; Yudhyadi, I.G.N.K.; Suartika, I.M.; Sari, N.H.
Dinamika Teknik Mesin: Jurnal Keilmuan dan Terapan Teknik Mesin Vol 9, No 2 (2019): Dinamika Teknik Mesin: Jurnal Keilmuan dan Terapan Teknik Mesin
Publisher : Universitas Mataram

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (427.568 KB) | DOI: 10.29303/dtm.v9i2.277

Abstract

This study aims to investigate the hardness properties of materials made of a mixture of aluminum, copper, and silicon carbide powders. The product has been made of mixtures aluminium (Al), copper (Cu) and silicon carbide (SiC) powders with a concentration of 80; 15; 5 (% wt), respectively. Manufacture of the specimens was conducted used powder metallurgy. The dimension of the specimens’ diameter of 25 mm and a thickness of 4 mm. The variation of the temperature sintering is 320, 420 and 520 oC for 40 minutes. The hardness properties have analyzed using the Brinell method. The results show that at the temperature range  320 - 420 oC, the hardness of the specimen increase to 15.2 BHN; it is due to the bond between metal powders is formed strong enough. Conversely, at 520 oC the hardness number is low because most of SiC is bound weakly to other powders. It can be concluded that the selection of temperature and sintering time and proper mixing greatly influence the hardness properties of materials yields of powder metallurgical.
Uji performansi motor listrik sebagai penggerak kendaraan listrik Mara, M.; Yudhyadi, I.G.N.K.; Adhi, I.G.A.K.C.; Setyawan, P.D.; Triadi, A.A.A.
Dinamika Teknik Mesin: Jurnal Keilmuan dan Terapan Teknik Mesin Vol 13, No 1 (2023): Dinamika Teknik Mesin: Jurnal Keilmuan dan Terapan Teknik Mesin
Publisher : Universitas Mataram

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.29303/dtm.v13i1.607

Abstract