Comparison Of Element Release From Glass Ionomer Cement With Various Coating Agents Eko Hadianto; Muhammad Dian Firdausy; Budi Suhartono; Salsa Sarah Aliza; Nadia Brilianti Firdausia; Erwid Fatchur Rahman; Grahita Aditya; Tahta Danifatis Sunnah
Media Dental Intelektual Vol. 8 No. 2 (2026): Media Dental Intelektual : August 2026
Publisher : Faculty of Dentistry, Universitas Islam Sultan Agung

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.30659/medali.8.2.162-170

Abstract

Background: GIC is very susceptible to contamination especially within 24 hours after mixing during the setting reaction. To protect against this, a coating agent can be applied. This study aims to determine the difference in fluoride release levels in Glass Ionomer Cement using coating agents such as EQUIA Coat, Varnish, and Cocoa Butter.Method: 21 cylindrical samples were prepared from conventional GIC (GC Fuji type II) and divided into 3 groups (groups I, II, and III) of 7 each. Group I samples were coated with EQUIA Forte Coat, group II with Varnish, and group III with Cocoa Butter. Each group of samples was stored in glass bottles soaked in distilled water for 7 days in an incubator at 37˚C. The fluoride release was measured using a 2010 DR spectrophotometer, while Alumina, natrium, Kalium, and Calcium releases were measured by an ICP-OES assay. The data obtained were analyzed comparatively using one-way ANOVA and the Kruskall-Wallis statistical test.Result: EQUIA Forte Coat showed the lowest concentration of released particles of Aluminum, Kalium, Natrium, and Fluoride, while the highest concentration was found in the Varnish group. Conclusion: The results concluded that EQUIA Forte Coat can seal GIC material well. Nevertheless, particles released in all groups are still considered to be safe for clinical usage.
Co-Authors Budi Suhartono Budi Suhartono Clarissa Bonita Syaravina Erwid Fatchur Rahman Fathimah Fitria Sa’adah Grahita Aditya Grahita Aditya Marzuki Akbar J. Dundu Moh Yusuf Moh Yusuf Muhammad Dian Firdausy, Muhammad Nadia Brilianti Firdausia Niluh Ringga Woroprobosari Nurfika Sofiana Nurul Rezki Utami Rizki Amalina Salsa Sarah Aliza Sandy Christiono Tahta Danifatis Sunnah