Article Per Year (5 Year)
p-Index From 2021 - 2026
0.817
P-Index
This Author published in this journals
All Journal Journal of Welding Technology Jurnal Mesin Sains Terapan
Al Fathier Al Fathier
Politeknik Negeri Lhokseumawe
Automotive Engineering Control & Systems Engineering Industrial & Manufacturing Engineering Materials Science & Nanotechnology Mechanical Engineering

Published : 5 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 2 Documents
Search
Journal : journal of welding technology

 1 
Pengaruh Variasi Temperatur PWHT Dan Tanpa PWHT Terhadap Sifat Kekerasan Baja ASTM A 106 Grade B Pada Proses Pengelasan SMAW Muhammad Femi Imanudin Purba; Al Fathier Al Fathier; Fakhriza Fakhriza
Journal of Welding Technology Vol 2, No 1 (2020): June
Publisher : Politeknik Negeri Lhokseumawe

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.30811/jowt.v2i1.1132

Abstract

Penelitian ini bertujuan untuk mengetahui nilai keseragaman kekerasan pada bagian-bagian yang terpengaruhi panas setelah dilakukan proses pengelasan dengan cara perlakuan panas atau Post Weld Heat Treatment (PWHT) yaitu pada daerah Base Metal, Heat Affected Zone (HAZ) dan Weldmetal. Penelitian ini menggunakan bahan baja ASTM A 106  Grade B, baja ini termasuk bahan karbon rendah. Menggunakan pengelasan SMAW dengan elektroda yang digunakan LB-52-18 Ø3,2. Pengujian kekerasan menggunakan mesin Hardness Test, ASTM A 106 Grade B Grade B ini merupakan baja karbon rendah dengan sedikit kandungan silikon beberapa hasil penelitian menemukan bahwa kandungan siliconnya adalah 0,03. Posisi pengelasan dengan menggunakan posisi pengelasan 1G atau ketika mengelas pipa berputar pada sumbu horizontal, jenis kampuh yang digunakan adalah kampuh V dengan sudut 70 o. Nilai kekerasan rata-rata spesimen yang tanpa perlakuan panas ini adalah Base Metal-1 (63,2) HAZ-1 (59,2) Weldmetal (60,67) HAZ-2 (62) dan Base Metal-2 (66,67). Dan adapun nilai kekerasan yang hampir mendekati dengan nilai kekerasan pada spesimen yang tanpa perlakuan panas adalah spesimen yang mendapat perlakuan panas dengan termperatur 400 derajat celcius dengan waktu pencapaian 30 menit dan ditahan dengan waktu 20 menit dengan nilai kekerasan rata-rata Base Metal-1 (72,17) HAZ-1 (59) Weldmetal (59,27) HAZ-2 (59,83) dan Base Metal-2 (72,5). Kata kunci :Pengelasan, Post Weld Heat Treatment (PWHT), Nilai Keseragaman Kekerasan
Effect of SMAW welding current variations on mechanical properties in ASTM A240 grade 304L Nurdin Nurdin; Al Fathier Al Fathier; Rizki Maulana; Fakhriza Fakhriza
Journal of Welding Technology Vol 7, No 2 (2025): December
Publisher : Politeknik Negeri Lhokseumawe

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.30811/jowt.v7i2.2509

Abstract

Welding current is one of the important parameters in the welding process, because inappropriate currents will result in welding defects in the welded material resulting in reduced weld joints. This study aims to determine the effect of current variations on SMAW welding joints ASTM A240 Grade 304L material on mechanical properties. This study uses ASTM A240 Grade 304L material with variations in welding currents of 80 A, 100 A, and 120 A using SMAW welding and using E308-16 electrodes with a diameter of 3.2 mm. Specimens were tested for chemical composition, visual test, penetrant test, and tensile test. Comparative data of tensile test explained that the highest tensile stress from variations in welding currents of 80 A, 100A, and 120 A was 625.27 MPa using a welding current of 100 A, the highest yield stress is 337.35 MPa, using a welding current of 100 A, and the highest elongation is 38.34% using a welding current of 100 A. From the data from the tensile test results for ASTM A240 Grade 304L material, the results obtained that the material data without welding treatment has the lowest tensile strength compared to with a group of variations in welding current. And the highest tensile strength value is in the 100 A current variation group.