Effect of Material Type and Minimum Diameter of Specimens on the Fatigue Life Syamsul Hadi; Anggit Murdani; Sudarmadji; Andhika Erlangga Setiawan Putra; Bambang Irawan; Hangga Wicaksono; Sza Sya Monica Valeria; Nila Alia
Logic : Jurnal Rancang Bangun dan Teknologi Vol. 21 No. 3 (2021): November
Publisher : Unit Publikasi Ilmiah, P3M, Politeknik Negeri Bali

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (2167.849 KB) | DOI: 10.31940/logic.v21i3.205-211

Abstract

The obstacle faced during the fatigue test is the waiting time which is quite long and inefficient, especially for test specimens made of ductile metal with waiting times of up to several days. The research method includes reducing the specimen radius to obtain a flexural stress approaching 400 MPa which was originally 229 MPa from a radius of 254 mm to 240 mm with the results of turning the original specimen obtained a minimum diameter of 8.6 mm is reduced to 7.3 mm at a maximum loading of 10 kg. Results of the research are brass specimens C3604BD type with a minimum diameter of 8.6 mm at a flexural stress of 298 MPa showing a fatigue life of 2455546 cycles with a test duration of 1754 minutes and a minimum specimen diameter of 7.3 mm at a flexural stress of 299 MPa showing a fatigue life of 684311 cycles with a test duration of 489 minutes which means that with a minimum specimen diameter of 7.3 mm the fatigue life is 3.59 times shorter than a minimum specimen diameter of 8.6 mm. Meanwhile, for aluminium AA1101 type with a minimum specimen diameter of 7.3 mm at a flexural stress of 182 MPa, the fatigue life is 422117 cycles with a test duration of 278 minutes and with a minimum specimen diameter of 8.6 mm at a flexural stress of 183 MPa, the fatigue life is 389232 cycles with a test duration of 302 minutes which means that with a minimum specimen diameter of 7.3 mm the fatigue life is 1.05 times shorter than the minimum specimen diameter of 8.6 mm or almost the same.
Pelatihan dan Pemasangan IP CAM CCTV untuk Meningkatkan Keamanan di RT 05 RW 10, Desa Kedungrejo Kabupaten Malang Sulistyono; Agus Dani; Elka Faizal; Nila Alia; Nurlia Sari
Jurnal Pengabdian Kepada Masyarakat Ceria (JPKMC) Vol. 1 No. 1 (2023): Jurnal Pengabdian Kepada Masyarakat Ceria (JPKMC)
Publisher : PT. Gelora Cipta Nusantara

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.61674/jpkmc.v1i1.11

Abstract

Desa Kedungrejo adalah salah satu desa yang berada di Kecamatan Pakis, Kabupaten Malang. Salah satu pemukiman warga yang terdapat di desa tersebut adalah pemukiman warga di RT/RW 05/10. Pemukiman warga RT/RW 05/10 Desa Kedungrejo berada di belakang perkebunan buah maupun sayuran, sehingga tidak terlihat dari jalan utama. Kondisi ini membuat daerah pemukiman tersebut perlu menyediakan infrastruktur terkait tindakan pencegahan terjadinya tindak kriminal, diantaranya adalah adanya CCTV. Sejalan dengan pemikiran di atas, dilakukan suatu kegiatan pemberdayaan masyarakat untuk mewujudkan lingkungan yang aman dan nyaman. Metode kegiatan ini diawali dengan analisis situasi kemudian dilanjutkan dengan survey dan observasi lokasi, selanjutnya persiapan kegiatan yang meliputi pembelian alat dan bahan, diikuti oleh pelatihan, pemasangan dan perakitan CCTV, yang terakhir adalah pelaporan dan evaluasi kegiatan pengabdian kepada masyarakat. Hasil yang didapat pada kegiatan ini adalah penambahan pengetahuan mitra tentang upaya peningkatan Keamanan lingkungan sekitar dengan penerapan teknologi digital berupa IP Camera CCTV serta terpasangnya 6 unit IP Camera CCTV Outdoor di lingkungan RT/RW 05/10, Desa Kedungrejo Kab. Malang