The effect of preheating on the color stability of microhybrid composite resin after immersion in carbonated beverages and black tea: an experimental study Nugroho, Raditya; Penga, Yohana Maria; Al Ghifari, Faiq Aqil; Wulandari, Erawati; Hidayati, Lusi
Padjadjaran Journal of Dentistry Vol 36, No 3 (2024): November 2024
Publisher : Faculty of Dentistry Universitas Padjadjaran

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.24198/pjd.vol36no3.58667

Introduction: Composite resin is commonly used in restorative dentistry due to its pleasing aesthetics. However, this material tends to experience discoloration, a vital standard reflecting the restoration’s success. Studies show that preheating is effective in maintaining the color stability of other types of composite resin; nevertheless, the effect on microhybrid composite resin is not fully understood. This study aimed to analyze the effect of preheating on the color stability of microhybrid composite resins after immersion in carbonated beverages and black tea. Method: Twenty-four Z250 shade A2 composite resin discs, each with a diameter of 7 mm and a thickness of 2 mm, were divided into four groups (n=6). While groups I and II underwent a preheating process at 68°C before being soaked in carbonated drinks and black tea, groups III and IV were prepared at room temperature (25°C) without preheating and soaked in carbonated drinks and black tea. The discoloration of the samples was determined utilizing a UV-Vis spectrophotometer according to CIEL*a*b* color space. Data were analyzed using one-way ANOVA followed by the Least Significant Difference (LSD) test. Result: Preheating increased the color stability of composite resins. Preheated composite resins experienced significantly lower discoloration than composite resins at room temperature after soaking in carbonated drinks and black tea (p<0.05). Conclusion: preheating can minimize the color change of microhybrid composite resin after immersion in carbonated beverages and black tea.

Comparison of the potential of green okra (Abelmoschus esculentus) extract and a combination of 17% EDTA and 2.5% NaOCl in removing the smear layer from dental root canal walls: experimental laboratory Nissa, Rahma Aulia; Nugroho, Raditya; Fatmawati, Dwi Warna Aju
Jurnal Kedokteran Gigi Universitas Padjadjaran Vol 36, No 2 (2024): Agustus 2024
Publisher : Fakultas Kedokteran Gigi Universitas Padjadjaran

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.24198/jkg.v36i2.56053

Introduction: The smear layer is a thin film of organic and inorganic substances that can inhibit intracanal medication penetration, necessitating removal with root canal irrigants. Commonly used irrigants include a combination of 17% EDTA and 2.5% NaOCl, but EDTA is ineffective against organic components, while NaOCl may cause periapical pain and instrument corrosion. Green okra extract contains active antibacterial compounds, showing potential as an alternative. This research aimed to compare the potential of green okra extract with that of 17% EDTA and 2,5% NaOCl in smear layer removal. Methods: This research is a laboratory experiment with a posttest only control group design. The treatment groups consisted of 12.5% green okra extract and a combination of 17% EDTA and 2,5% NaOCl root canal irrigation agents. Ten mandibular premolars were sectioned at the cemento-enamel junction then prepared using step-back technique. Five samples were irrigated with 0,1 ml of 12.5% green okra extract, while the other five received 0,1 ml 17% EDTA and 2.5% NaOCl. The cleanliness of the root canal walls was evaluated using a Scanning Electron Microscope (SEM) at 5000x magnification, and data were analyzed using the Mann-Whitney U test. Result: Both groups exhibited similar levels of root canal cleanliness (p=0.093), with a cleanliness score of 2, indicating mostly open dentin tubule orifices and minimal smear layer. Conclusion: Green okra extract (12.5) demonstrated comparable potential to a combination of 17% EDTA and 2.5% NaOCl in removing the smear layer from root canal walls.Perbandingan potensi ekstrak okra hijau (Abelmoscus esculentus) dengan kombinasi EDTA 17% dan NaOCl 2,5% dalam membersihkan smear layer dinding saluran akar gigi: eksperimental laboratorisPendahuluan: Smear layer adalah lapisan tipis yang berisi substansi organik dan anorganik. Smear layer dapat menghambat penetrasi medikamen intrakanal ke dalam tubulus dentin sehingga harus dibersihkan dengan bahan irigasi saluran akar. Bahan irigasi saluran akar yang biasa digunakan adalah kombinasi EDTA 17% dan NaOCl 2,5%. Namun, EDTA 17% tidak dapat membersihkan substansi organik dari smear layer, sedangkan NaOCl 2,5% dapat menimbulkan nyeri pada jaringan periapikal serta menimbulkan korosi instrumen endodontik. Ekstrak okra hijau mengandung senyawa antibakteri aktif, sehingga berpotensi sebagai alternatif bahan irigasi. Penelitian ini bertujuan untuk menganalisis perbandingan potensi ekstrak okra hijau dengan kombinasi EDTA 17% dan NaOCl 2,5% dalam membersihkan smear layer dinding saluran akar gigi. Metode: Jenis penelitian eksperimental laboratoris dengan rancangan posttest only control group design. Kelompok perlakuan konsentrasi ekstrak okra hijau 12,5% dan kombinasi EDTA 17% dan NaOCl 2,5%. Sepuluh premolar mandibula dipotong di cemento-enamel junction kemudian dipreparasi menggunakan teknik step back. Lima sampel di irigasi dengan ekstrak okra hijau 12,5% sebanyak 0,1 ml dan lima sampel di irigasi dengan EDTA 17% sebanyak 0,1 ml 17% dan NaOCl 2,5% sebanyak 0,1. Sepuluh sampel dinilai skor kebersihan dinding saluran akarnya menggunakan Scanning Electron Microscope (SEM) dengan perbesaran 5000x dan dilakukan uji beda menggunakan Mann Whitney U test. Hasil: Kebersihan dinding saluran akar pada dua kelompok sampel memiliki tingkat kebersihan yang sama. Analisis data menggunakan Mann Whitney U test. diperoleh nilai p=0,093 yang berarti bahwa tidak ada perbedaan yang signifikan antara dua kelompok. Kedua kelompok memiliki skor 2, artinya sebagian besar orifis tubuli dentin terbuka dan terdapat sedikit smear layer. Simpulan: Ekstrak okra hijau 12,5% mempunyai potensi yang sama dengan kombinasi larutan EDTA 17% dan irigasi NaOCl 2,5% dalam membersihkan smear layer dinding saluran akar.

Potensi ekstrak buah okra hijau (Abelmoscus esculentus) dalam membersihkan smear layer pada kavitas dentin mahkota: penelitian eksperimental laboratoris Ismanto, Berliana Inas Nabila Putri; Aju Fatmawati, Dwi Warna; Nugroho, Raditya; Lestari, Sri
Jurnal Kedokteran Gigi Universitas Padjadjaran Vol 37, No 1 (2025): April 2025
Publisher : Fakultas Kedokteran Gigi Universitas Padjadjaran

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.24198/jkg.v37i1.58588

Pendahuluan:Smear layer merupakan suatu lapisan yang terbentuk dari sisa-sisa debris pasca instrumentasi yang tersusun dari komponen organik dan anorganik. Smear layer yang tidak dibersihkan dapat mengganggu pelekatan suatu bahan restorasi ke dalam dinding kavitas serta dapat menjadi host bagi mikroorganisme.. Salah satu bahan dentin conditioner yang biasa digunakan adalah asam poliakrilat 10%. Bahan alami yang dapat digunakan sebagai alternatif dentin conditioner untuk meminimalisir efek samping bahan kimia adalah ekstrak buah okra hijau karena memiliki kandungan yang bersifat asam dan mengandung senyawa saponin yang bersifat sebagai surfaktan alami. Penelitian ini bertujuan untuk mengetahui kemampuan ekstrak buah okra hijau dalam membersihkan smear layer pada permukaan kavitas dan membandingkan kemampuan ekstrak buah okra hijau dengan asam poliakrilat 10% dalam membersihkan smear layer. Metode: Penelitian yang dilakukan merupakan jenis penelitian eksperimental laboratoris untuk mengetahui kemampuan ekstrak buah okra hijau 12,5% dalam membersihkan smear layer dibandingkan dengan asam poliakrilat 10%. 10 elemen gigi dilakukan preparasi kavitas kelas I pada 1/3 tengah permukaan bukal hingga terbentuk kavitas dengan diameter 3 mm dan kedalaman 2 mm. Lima sampel diaplikasikan dengan asam poliakrilat 10% dan lima sampel diaplikasikan dengan ekstrak buah okra hijau 12,5% sebanyak 6 µL, dibiarkan selama 20 detik, diirigasi kembali dengan aquades 0,5 ml, dan dikeringkan dengan cotton pellet. Setiap sampel dilakukan pemotretan dengan SEM perbesaran 5000x. Hasil pemotretan dilakukan penilaian oleh 3 orang pengamat sesuai skor yang ada. Hasil: Hasil penelitian menunjukkan bahwa kebersihan permukaan kavitas pada kedua kelompok sampel memiliki nilai modus yang sama yaitu 2 (sebagian orifis tubuli dentin terbuka dan terdapat sedikit smear layer). Simpulan: Ekstrak buah okra hijau 12,5% mempunyai kemampuan membersihkan smear layer pada dentin mahkota setara dengan asam poliakrilat 10%.The potential of green okra fruit extract (Abelmoscus esculentus) for cleaning the smear layer on crown dentin cavity: experimental laboratory studyIntroduction: Smear layer is a thin layer formed by post-instrumentation of tooth structure. Smear layers can inhibit dental material bonding to the cavity and can affect as a host for microorganisms. Partial smear layer should be removed using dentin conditioner. One of the commonly used dentin conditioners is 10% polyacrylic acid. The natural ingredient could be used as an alternative dentin conditioner to minimize the side effects of the chemical material above is 12.5% green okra extract because it contains acid and saponin which act as natural surfactants. The aim of the research was to determine the ability of green okra fruit extract to clean the smear layer on cavity surfaces compared to 10% polyacrylic acid. Methods: The research was a laboratory experimental study to determine the ability of 12.5% green okra extract to remove the crown dentin smear layer compared to 10% polyacrylic acid. Ten dental elements were prepared for class I cavity on the middle 1/3 of the buccal surface until reaching a cavity with a diameter of 3 mm and a depth of 2 mm was formed. Five samples were applied with 10% polyacrylic acid and 5 samples were applied with 12.5% green okra fruit extract, 6 µL each group, left for 20 seconds then irrigated with 0.5 ml aquadest and dried with cotton pellet. The samples were examined for their cavity cleanliness score using Scanning electron microscope (SEM) photo with 5000x of magnification. The image results were assessed by 3 observers according to the existing scores. Results: The results showed that the cleanliness of the cavity surface in both sample groups had the same level of cleanliness, score 2 (some of the dentin tubule orifices are open and there is a small smear layer). Both groups have the same score and statistical tests show that there is no significant difference between them. Conclusion: 12.5% green okra fruit extract has the ability to clean the smear layer on crown dentin equal to 10% polyacrylic acid.

The Effect of Glycerin Application on The Surface of Microhybrid Composite Resin to Its Compressive Strength with Immersed in Pure Coffee Solution Amala, Farina Nur; Nugroho, Raditya; Lestari, Sri
Journal of Indonesian Dental Association Vol 5 No 1 (2022): April
Publisher : Indonesian Dental Association

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.32793/jida.v5i1.744

Introduction: There are various restoration materials, one of which is microhybrid composite resin. An effective way to increase its compressive strength is by applying glycerin before curing. This can minimize the formation of a layer of OIL (Oxygen inhibition layer) which is formed due to polymerization that interrupted by the contact of composite resin with oxygen. Exposure with acidic solution such as pure coffee solution causing the occurrence of matrix degradation which can decrease the compressive strength of microhybrid composit. The longer its immersed in pure coffee solution, the more polymer bonds are broken and releasing monomer which result in a decrease of compressive strength. Objective: This study aimed to reveal the effects of glycerin application on the compressive strength of microhybrid composite resins immersed in pure coffee solution. Methods: There are 6 sample groups of composite resin namely: group SG, group S, group GK16, group K16, group GK32, and group K32 with 4 samples per group. Each sample made of microhybrid composite resin brand Filtek Z250 shaped disc with a diameter of 4 mm and thickness of 2 mm. Glycerin was applied to the surfaces of three groups before curing, while other groups were not. After treatment, all samples are compressive strength tested using Universal Testing Machine. The data were analyzed using the Two Way ANOVA followed by Post-Hoc LSD test. Result: The groups with glycerin had higher compressive strength than those groups without glycerin application. The non-immersed groups had a higher hardness level than those groups which were immersed. The Two-Way ANOVA test confirmed that there was a statistically significant difference (p<0.05) among all groups. Conclusion: Glycerin application can increase the compressive strength of microhybrid composite resin immersed in pure coffee solution by minimizing OIL formation on its surface. ABSTRAK Pendahuluan: Terdapat berbagai bahan restorasi, salah satunya yaitu resin komposit microhybrid. Cara yang efektif untuk meningkatkan kekuatan tekan resin komposit microhybrid adalah mengoleskan gliserin sebelum curing. Hal ini dapat meminimalisir pembentukan OIL (Oxygen Inhibition Layer) pada permukaan komposit yang terbentuk akibat polimerisasi terganggu oleh kontak resin komposit dengan oksigen. Kontak dengan larutan bersifat asam seperti larutan kopi murni mampu menyebabkan terjadinya degradasi matriks yang dapat menurunkan kuat tekan komposit microhybrid. Semakin lama resin komposit microhybrid direndam dalam larutan kopi murni, maka semakin banyak polimer yang terputus dan melepaskan monomernya yang berakibat penurunan kekuatan tekan. Tujuan: Untuk mengetahui pengaruh aplikasi gliserin terhadap kekuatan tekan resin komposit microhybrid dalam perendaman larutan kopi murni. Metode: Sampel dibagi menjadi 3 kelompok yaitu kelompok kontrol (sebelum perendaman), kelompok perlakuan (diaplikasi gliserin), kelompok perlakuan (tanpa aplikasi gliserin). Tiap sampel dibuat dari resin komposit microhybrid merk Filtek Z250 dibentuk cakram dengan diameter 4 mm dan ketebalan 2 mm. Gliserin diaplikasikan di atas permukaan resin komposit pada tiga kelompok, sedangkan kelompok lainnya tidak. Setelah perlakuan, semua kelompok dilakukan uji kekuatan tekan menggunakan Universal Testing Machine. Data dianalisa menggunakan Two Way Anova dilanjutkan dengan uji Post-Hoc LSD. Hasil: Kekuatan tekan kelompok dengan aplikasi gliserin lebih tinggi dibandingkan tanpa gliserin. Selain itu, kelompok tanpa perendaman dalam larutan kopi murni memiliki kekuatan tekan lebih tinggi dibandingkan dengan perendaman. Hasil uji Two Way ANOVA menunjukkan adanya perbedaan signifikan (p<0,05) antar semua kelompok. Kesimpulan: Aplikasi gliserin dapat meningkatkan kekuatan tekan resin komposit microhybrid dalam perendaman larutan kopi murni melalui minimalisir pembentukan OIL pada permukaannya.

Effect of Glycerin Application on Discoloration of Nanofiller Composite in Instant Coffee Saetikho, Saraswita Gabrillah; Lestari, Sri; Nugroho, Raditya
Journal of Indonesian Dental Association Vol 5 No 1 (2022): April
Publisher : Indonesian Dental Association

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.32793/jida.v5i1.749

Introduction: Most modern society assumes that an attractive appearance is a necessity, including the aesthetics of dental restorations. Nanofiller composite resins are widely used because they can reduce polymerization shrinkage and produce a smooth surface that improves aesthetics. Composite resins can change color due to extrinsic factors such as exposure to exogenous materials, one of which is instant coffee and intrinsic factors such as disruption of the polymerization process. Composite resins can experience polymerization disturbances when their surfaces are exposed to air before being irradiated, thereby disrupting the polymerization process. This is indicated by the formation of an oxygen inhibitor layer (OIL) this layer can reduce the quality of the restoration. This layer cannot be completely removed but the application of glycerin can reduce the formation of the layer. Objectives: To determine the degree of discoloration of nanofiller composite resin coated with glycerin and not due to immersion in instant coffee solution. Methods: The composite resin sample was in the form of a disc with a diameter of 10 mm and a thickness of 2 mm, coated and uncoated with glycerin before irradiation. Samples were immersed in the instant coffee solution for 37 hours and 61 hours. Color changes were observed using the Minolta CR-10 Color Reader. Results: The most obvious color change was in the nanofiller composite resin group that was not coated with glycerin, with an E value of 1.04 with an immersion time of 61 hours. The least color change in the glycerin-coated nanofiller composite resin group, with an E value of 0.91. there was a significant difference in the color changes of the sample group with glycerin and non-glycerin applications. Conclusion: There was color change in the nanofiller composite resin coated with glycerin and non-glycerin. The least color change was in the glycerin-coated group. ABSTRAK Pendahuluan: Sebagian masyarakat modern beranggapan bahwa penampilan yang menarik merupakan suatu kebutuhan, termasuk estetik restorasi gigi. Resin komposit nanofiller banyak digunakan karena dapat mengurangi polymerization shrinkage dan menghasilkan permukaan yang halus sehingga meningkatkan estetik. Resin komposit dapat mengalami perubahan warna akibat faktor ekstrinsik seperti terpapar bahan eksogen salah satunya adalah kopi instan dan faktor intrisik seperti terganggunya proses polimerisasi. Resin komposit dapat mengalami gangguan polimerisasi ketika permukaannya terpapar udara sebelum disinar, sehingga menyebabkan terganggunya proses polimerisasi. Hal ini ditandai dengan terbentuknya lapisan oxygen inhibitor layer (OIL) lapisan ini dapat mengurangi kualitas restorasi. Lapisan ini tidak dapat sepenuhnya dihilangkan tetapi aplikasi gliserin dapat mengurangi pembentukan lapisan tersebut. Tujuan: Mengetahui tingkat perubahan warna resin komposit nanofiller dengan dan non gliserin akibat perendaman larutan kopi instan. Metode: Sampel resin komposit berbentuk cakram diameter 10 mm tebal 2 mm, dengan dan non gliserin sebelum disinar. Sampel direndam dalam larutan kopi instan selama 37 jam dan 61 jam. Perubahan warna diamati dengan menggunakan alat Color Reader Minolta CR-10. Hasil: Perubahan warna terbesar pada kelompok resin komposit nanofiller non gliserin, dengan nilai ΔE 1,04 dengan waktu perendaman 61 jam. Perubahan warna terkecil pada kelompok resin komposit nanofiller yang dilapisi gliserin, dengan nilai ΔE 0,91 dengan waktu perendaman 61 jam. Terdapat perbedaan bermakna pada kelompok sampel dengan dan non gliserin. Kesimpulan: Terjadi perubahan warna pada resin komposit nanofiller yang dilapisi gliserin dan non gliserin. Perubahan warna yang terkecil terjadi pada kelompok yang dilapisi gliserin.

UJI ANTIBAKTERI EKSTRAK BUAH OKRA HIJAU (Abelmoschus esculentus) KONSENTRASI 12,5%, 25%, 50% DAN 100% TERHADAP BAKTERI Streptococcus mitis: penelitian eksperimental Farizki, Helmy Affan; Lestari, Sri; Wulandari, Erawati; Fatmawati, Dwi Warna Aju; Rakhmadian, Ratih Delio; Nugroho, Raditya
Jurnal Kedokteran Gigi Universitas Padjadjaran Vol 36, No 1 (2024): April 2024
Publisher : Fakultas Kedokteran Gigi Universitas Padjadjaran

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.24198/jkg.v36i1.52835

Pendahuluan: Nekrosis pulpa adalah kondisi terjadinya kematian sel di dalam rongga pulpa dan saluran akar sebagai akibat dari karies gigi. Bakteri yang berperan dalam karies gigi hingga nekrosis pulpa yaitu S. mitis yang merupakan spesies alfa-hemolitik mesofil Streptococcus yang berkembang dalam mulut manusia yang umum ditemukan di tenggorokan, nasofaring, dan mulut. Tujuan penelitian menganalisis antibakteri ekstrak buah okra hijau (Abelmoschus esculentus) dibandingkan dengan NaOCL dan EDTA terhadap S. mitis. Metode: Jenis penelitian eksperimental laboratoris dengan pendekatan posttest only control group design. Terdapat 2 kelompok kontrol yaitu NaOCl 2,5% dan EDTA 17% serta 6 kelompok perlakuan yaitu ekstrak buah okra hijau konsentrasi 12,5, 25, 50 dan 100%. Buah okra hijau yang akan dikembangkan sebagai bahan irigasi diidentifikasi dan diekstraksi menggunakan metode maserasi dengan etanol 96% hingga menghasilkan ekstrak kental konsentrasi 100%. Hasil: Terdapat peningkatan diameter zona hambat ekstrak buah okra hijau (Abelmoschus esculentus) terjadi mulai dari konsentrasi ekstrak 12,5, 25, 50% dan 100%. Rerata diameter zona hambat dari yang terkecil hingga terbesar yaitu ekstrak buah okra hijau konsentrasi 12,5% (10,51 mm), 25% (13,67 mm), 50% (15,15 mm), dan 100% (17,54 mm). Data dianalisis menggunakan uji normalitas Shapiro-Wilk, uji homogenitas Levene, dan uji Kruskall-Wallis dengan hasil nilai p=0,000 atau p<0,05. Simpulan: Ekstrak buah okra hijau (Abelmoschus esculentus) dengan konsentrasi 12,5, 25, 50%, dan 100% memiliki daya antibakteri yang lebih kecil jika dibandingkan dengan NaOCl 2,5% dan EDTA 17% dalam menghambat pertumbuhan bakteri S. mitis.

Title

Found 6 Documents
Search

Abstract

Abstract

Abstract

Abstract

Abstract

Abstract

Title Search

Found 6 Documents Search

Abstract

Abstract

Abstract

Abstract

Abstract

Abstract

Title

Found 6 Documents
Search