Article Per Year (5 Year)
p-Index From 2021 - 2026
0
P-Index
This Author published in this journals
All Journal Jurnal Ilmu Dasar Jurnal Teori dan Aplikasi Fisika JASIEK (Jurnal Aplikasi Sains, Informasi, Elektronika dan Komputer)
Simon Sembiring
Department of Physics, Faculty of Mathematics and Natural Sciences, Universitas Lampung, Lampung 35145
Computer Science & IT Control & Systems Engineering Decision Sciences, Operations Research & Management Electrical & Electronics Engineering Materials Science & Nanotechnology Mathematics Physics

Published : 14 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 14 Documents
Search

 1   2 
Pengaruh Suhu Sintering Terhadap Karakteristik Fisis Komposit MgO-SiO2 Berbasis Silika Sekam Padi Dian Dahliana; Simon Sembiring; Wasinton Simanjuntak
Jurnal Teori dan Aplikasi Fisika Vol 1, No 1 (2013): Jurnal Teori dan Aplikasi Fisika
Publisher : Universitas Lampung

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.23960/jtaf.v1i1.477

Abstract

Dalam penelitian ini komposit MgO-SiO2 dengan perbandingan massa MgO-SiO2 3:2 telah dibuat menggunakan metode sol-gel dari magnesium nitrat heksahidrat (Mg(NO3)2.6H2O) dan silika yang diperoleh dari sekam padi. Pembuatan komposit dilakukan dengan mencampur bahan baku di bawah pengadukan selama satu jam untuk menghasilkan gel komposit. Gel dikeringkan pada suhu 110 ºC selama 24 jam dan gel kering dijadikan serbuk, kemudian disintering pada suhu yang berbeda dari 1000, 1100, 1200 dan 1300 ºC. Karakterisasi sampel dilakukan untuk menentukan densitas, porositas dan kekerasan. Pengukuran densitas menunjukkan bahwa semakin tinggi suhu sintering, densitas semakin meningkat, sedangkan untuk porositas terjadi sebaliknya. Untuk kekerasan, semakin tinggi suhu sintering, semakin tinggi kekerasan yang sesuai dengan meningkatnya densitas dan menurunnya porositas.
Pengaruh pH Terhadap Distribusi Ukuran Partikel Alumina yang Dihasilkan Secara Elektrokimia Lidiya Permata Dewi; Simon Sembiring; Wasinton Simanjuntak
Jurnal Teori dan Aplikasi Fisika Vol 3, No 1 (2015): Jurnal Teori dan Aplikasi Fisika
Publisher : Universitas Lampung

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.23960/jtaf.v3i1.1287

Abstract

Dalam penelitian ini, metode elektrokimia digunakan untuk menghasilkan alumina, dengan tujuan untuk mengetahui pengaruh pH pada jumlah dan distribusi ukuran partikel dari alumina yang dihasilkan. Pembentukan alumina dilakukan pada potensial yang tetap yakni 22 volt, dengan pH yang berbeda yakni 4,5, dan 6. Alumina yang dihasilkan kemudian dikeringkan dengan oven dengan suhu 100oC dan selanjutnya digerus menjadi serbuk. Sampel serbuk yang dihasilkan kemudian dikarakterisasi menggunakan alat analisis ukuran partikel untuk mengetahui distribusi ukuran partikel dari sampel. Hasil menunjukkan bahwa pH mempengaruhi jumlah dan ukuran partikel dari sampel. Dalam hal jumlah, diketahui bahwa semakin besar pH, semakin sedikit alumina yang dihasilkan, dan untuk alasan ini, pH 4 adalah yang optimum, sementara dalam hal ukuran partikel, berlaku sebaliknya.
PengaruhPenambahan Alumina (0 dan 10wt%) Terhadap Karakteristik Termal (DTA-TGA) dan Konduktivitas Termal Bahan Keramik Cordierite Berbasis Silika Sekam Padi Nesya Tamalia; Simon Sembiring; Wasinton Simanjuntak
Jurnal Teori dan Aplikasi Fisika Vol 5, No 1 (2017): Jurnal Teori dan Aplikasi Fisika
Publisher : Universitas Lampung

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.23960/jtaf.v5i1.1365

Abstract

This study was carried out to investigate the effect ofalumina on the physicalcharacteristics, microstructure, andelectrical conductivity of cordierite. Silica obtained from rice husk through sol-gel method, while alumina and magnesium were obtained from Sigma-Aldrich. Cordierite was synthesizedbythe solid state method and sintered at1200°C. The measurement results revealed that the addition of alumina on cordierite reduceddensity and increasedporosity. The Differensial Thermal Analysis (DTA) at 694oC for C1 and 649,9oC for C2showed that there iscristobalite phase of rice husk and spinel phase has also been established. The results of the thermal conductivity C2 is high at 12.97 W/mKbecause a sample is homogeneous.
Karakteristik Termal (DTA/TGA) dan Konduktivitas Termal Cordierite (2MgO.2Al2O3.5SiO2) Berbasis Silika Sekam Padi Akibat Penambahan MgO (0, 10, 15%berat) Annisa Rizka Amalia; Simon Sembiring; Wasinton Simanjuntak
Jurnal Teori dan Aplikasi Fisika Vol 5, No 1 (2017): Jurnal Teori dan Aplikasi Fisika
Publisher : Universitas Lampung

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.23960/jtaf.v5i1.1360

Abstract

Synthesis and characterization of cordierite-based rice husk silica has been conducted by MgO 0, 10, and 15wt%. Preparation of cordierite used MgO, Al2O3, and silica rice husk. Silica was extracted by alkalis method using 1,5 NaOH solution and 10% HNO3. The samples were sintered at temperature of 1250°C. The characteristics of thermal were analysed by DTA/TGA and thermal conductivity were analysed by ASTM E1530, while physics characterization were anlysed by density and porosity. DTA/TGA result showed that the crystallization process of cordierite through spinel bonding. The thermal conductivity values obtained were between 2,9089-3,1647 (W/m.K). Based on the result, it can be concluded that the addition of MgO on cordierite increased thermal conductivity and porosity as well as reduced density.
Co-Authors Ade Lia Tristiana Anggita Maharani Annisa Rizka Amalia Aris Pratama Bambang Joko Suroto Desyandri Desyandri Dian Dahliana Ediman Ginting Suka Kamisah D Pandiangan Lidiya Permata Dewi Mardova, Liyana Nesya Tamalia Pandapotan Tambunan Prastiana Tiara Pratiwi Pulung Karo-Karo Putri Hanifah Liani Rudy Situmeang Suprihatin Suprihatin Vinindia Kusuma Wasinton Simanjuntak