Article Per Year (5 Year)
p-Index From 2020 - 2025
4.731
P-Index
This Author published in this journals
All Journal Indonesian Journal of Geography Al-Fiziya: Journal of Materials Science, Geophysics, Instrumentation and Theoretical Physics POSITRON Jurnal Penelitian Fisika dan Aplikasinya (JPFA) Jurnal Sains dan Teknologi Komunikasi Fisika Indonesia TELKOMNIKA (Telecommunication Computing Electronics and Control) Indonesian Journal of Electrical Engineering and Informatics (IJEEI) Journal of Aceh Physics Society Jurnal Litbang Industri JOURNAL ONLINE OF PHYSICS Jurnal Fisika FLUX Proceeding of the Electrical Engineering Computer Science and Informatics Jurnal Ilmiah Pertanian JMPM (Jurnal Material dan Proses Manufaktur) Jurnal Pengabdian UntukMu NegeRI Journal of Research and Technology JURNAL PHOTON Indonesian Physical Review Science, Technology, and Communication Journal
Romi Fadli Syahputra
Department Of Physics, Faculty Of Mathematics, Natural Sciences & Health, Universitas Muhammadiyah Riau, Pekanbaru, Indonesia
Religion Agriculture, Biological Sciences & Forestry Astronomy Chemical Engineering, Chemistry & Bioengineering Chemistry Computer Science & IT Earth & Planetary Sciences Economics, Econometrics & Finance Education Electrical & Electronics Engineering Energy Engineering Environmental Science Industrial & Manufacturing Engineering Law, Crime, Criminology & Criminal Justice Materials Science & Nanotechnology Mechanical Engineering Nursing Physics Social Sciences

Published : 38 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 2 Documents
Search
Journal : JMPM (Jurnal Material dan Proses Manufaktur)

 1 
Biokomposit Papan Partikel diperkuat Serat Alam Sabut Kelapa dan Tempurung Kelapa dan matriks epoksi Delovita Ginting; Romi Fadli Syahputra; Wirdatul Jannah
JMPM (Jurnal Material dan Proses Manufaktur) Vol 7, No 1 (2023): Juni
Publisher : Universitas Muhammadiyah Yogyakarta

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.18196/jmpm.v7i1.18375

Abstract

Papan partikel serat alami (biokomposit) dapat dijadikan alternatif pengganti material konvensional karena ramah lingkungan, sumber terbarukan dan sifatnya yang dapat terurai secara alami. Penelitian ini menyajikan studi tentang karakterisasi mekanik dan fisis papan partikel polimer diperkuat serat alam yaitu sabut kelapa dan tempurung kelapa. Variabel tetap dalam penelitian ini adalah jumlah fraksi matriks yaitu resin eposki. Variabel fraksi massa penyusun papan partikel dalam penelitian ini yaitu sabut kelapa:tempurung kelapa :epoksi adalah PP1 (30:0:70), PP2 (22,5:7,5:70), PP3 (15:15:70), PP4 (7,5:22,5:70), dan PP5 (0:30:70). Papan partikel diuji kelenturannya menggunakan mesin Universal Testing Machine mengacu pada ASTM D 7-90-03, ketangguhan impak sampel menggunakan mesin Impact Tester mengacu pada ASTM D 6110. Sampel diuji kerapatan dan pengembangan tebalnya mengacu SNI 03-2105-2006. Hasil pengujian sampel menunjukkan nilai kerapatan optimum pada sampel PP3 yaitu sebesar 1,05 g/cm3 dengan sampel diperkuat sabut kelapa dan tempurung kelapa. Hasil pengujian nilai uji ketangguhan impak optimum pada sampel PP5 yaitu sebesar 3.20 J/cm2 dan hasil pengujian nilai uji kuat lentur optimum pada sampel PP5 yaitu 382,29 Kgf/cm2 dengan sampel diperkuat tempurung kelapa. Natural fiber particle board (biocomposite) can be used as an alternative to conventional materials because it is environmentally friendly, a renewable source and is naturally biodegradable. This research presents a study on the mechanical and physical characterization of natural fiber reinforced polymer particle board, namely coconut coir and coconut shell. The fixed variable in this study was the number of matrix fractions, namely epoch resin. The variable mass fraction of the particle board in this study was coconut coir:coconut shell:epoxy was PP1 (30:0:70), PP2 (22,5:7,5:70), PP3 (15:15:70), PP4 (7,5:22,5:70), and PP5 (0:30:70). Particle board was tested for flexibility using the Universal Testing Machine referring to ASTM D 7-90-03, the impact toughness of the samples using the Impact Tester machine referring to ASTM D 6110. The samples were tested for density and thickness expansion referring to SNI 03-2105-2006. The results of the sample testing showed that the optimum density value for the PP3 sample was 1.05 g/cm3 for the reinforced coconut coir and coconut shell samples. The test results for the optimum impact toughness test value on the PP5 sample were 3.20 J/cm2 and the test results for the optimum flexural strength test value on the PP5 sample were 382.29 Kgf/cm2 with the coconut shell reinforced sample.
Fabrikasi Papan Serat Tandan Kosong Kelapa Sawit dengan Penambahan Bahan Fluoresensi Fosfor Husna, Ropiqotul; Yana, Debi; Kusmawati, Intan; Aisah, Nurul; Ginting, Delovita; Syahputra, Romi Fadli
JMPM (Jurnal Material dan Proses Manufaktur) Vol. 7 No. 2 (2023): Desember
Publisher : Universitas Muhammadiyah Yogyakarta

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.18196/jmpm.v7i2.19615

Abstract

Serat bahan alam dapat dijadikan pengganti material komposit yang ramah lingkungan. Serat tandan kosong kelapa sawit (TKKS) merupakan salah satu serat alam hasil pengolahan industri kelapa sawit yang tersedia dalam jumlah yang besar. Pemfaatan serat TKKS sebagai papan serat yang inovatif belum banyak dikaji secara fisis. Penambahan zat aditif fluorosensi memberikan keunggulan produk kayu maupun papan serat agar memiliki nilai estetika yang tinggi. Tujuan penelitian ini memfabrikasi biokomposit papan serat inovatif berbasis serat TKKS dengan penambahan bahan fluoresensi fosfor. Papan serat difabrikasi dengan metode hand lay-up dan cold compaction. Komposisi utama papan serat terdiri atas serat TKKS, resin epoxy, dan 5 g bubuk posfor. Kandungan serat TKKS divariasikan mulai dari 76% sampai 86%. Hasil pengujian fisis menunjukkan nilai densitas papan serat berkisar 0,34 - 0,59 g/cm³ dan daya serap airnya 105,22 - 156,475%. Nilai kapasitas panas spesifik papan serat berikisar 0,34 - 2,2 J/g˚C dan konduktivitas termalnya 0,001-0,002 W/mK. Sementara, besar bending strength sebesar 1,30 – 6,42 Mpa yang relatif sebanding dengan papan serat bio-komposit. Penambahan fosfor berpengaruh terhadap sifat termal papan serat, sehingga cukup baik bila diaplikasikan sebagai bio-insulator yang memiliki fitur fluorosensi.
Co-Authors -, Yeeri Badrun Adila Fitri Yani Yani Ahmad Nurhuda Aisah, Nurul Andika Thoibah Andri Saputra Anggraini, Wresni Anggreani, Selvia Anita, Sofia Ariyani Ayu Risti Candini Basdyo, Doni Candini, Ayu Risti Dadang Syarif Sihabudin Sahid Dalimunthe, Latipa Hannum Dedi Irawan Dedi Irawan Defrianto Defrianto Delovita Ginting, Delovita Dino Yanuardi Doni Basdyo Elsie Erman Taer Fitra Perdana Fitri, Ade Haryana bin Mohd Hairi Haryana Hairi Haryana Hairi Hikma, Nurfi Husna, Ropiqotul Ismail, Noor Maizura Ismaliyah, Dhea ISRAWATI HARAHAP Iwantono Iwan Barnawi Izzah, Ramy Fitrah Khaikal Ramadhan Kusmawati, Intan Lailatul Munawaroh Laras Sita Widara Leli Nurhamiyah Lubis, Viviana Mesra Sania Moh Danil Hendry Gamal Mubarak Mubarak Neneng Fitrya Nopripa Herlina Novia Gesriantuti Nurhamiyah, Leli Okfalisa Okfalisa Okfalisa Okfalisa Okfalisa Okfalisa Okfalisa Okfalisa Okfalisa Okfalisa Okfalisa Okfalisa Okfalisa, Okfalisa Piza Piza Piza, Piza Prastiwi, Adila Pramudiah Rachmawati Rachmawati Rezki, Yona Purnama Riad Syech Ridho Kurniawan Rifardi Rina Amelia Rismadani Haryanti Roby Ikhsan Ros Meri S. P. Dewi Saktioto Saktioto Sasmita Sasmita Shabri Putra Wirman Siti Hardiyanti Soerbakti, Yan Sri Fitria Retnawaty Sri Mulyani Syamsudhuha Syamsudhuha Tri Adelia Vepy Asyana Viviana Lubis Viviana Lubis Wahyu Candra Welly, Indah Sri wirdatul jannah Wresni Anggraini Wulandari, Surya Yan Soerbakti Yan Soerbakti Yan Soerbakti Yana, Debi Yani, Adila Fitri Yoli Zairmi Yulia Fitri Yunita I. Lubis Zairmi, Yoli Zamri, Zamri Zulkarnain Zulkarnain