All Journal Jurnal Sains Materi Indonesia Komunikasi Fisika Indonesia Jurnal Fisika Unand Prosiding SNFA (Seminar Nasional Fisika dan Aplikasinya) Jurnal Hilirisasi IPTEKS (JHI) Jurnal Ilmu Fisika INTEGRITAS : Jurnal Pengabdian BERNAS: Jurnal Pengabdian Kepada Masyarakat Jurnal Pengabdian kepada Masyarakat Nusantara Warta Pengabdian Andalas: Jurnal Ilmiah Pengembangan Dan Penerapan Ipteks PROSIDING SEMINAR NASIONAL FISIKA (E-JOURNAL) Indonesian Journal of Community Empowerment and Service
Alimin Mahyudin
Jurusan Fisika FMIPA Universitas Andalas
Religion Agriculture, Biological Sciences & Forestry Humanities Astronomy Biochemistry, Genetics & Molecular Biology Computer Science & IT Decision Sciences, Operations Research & Management Dentistry Earth & Planetary Sciences Economics, Econometrics & Finance Education Electrical & Electronics Engineering Energy Engineering Environmental Science Health Professions Languange, Linguistic, Communication & Media Law, Crime, Criminology & Criminal Justice Materials Science & Nanotechnology Mathematics Medicine & Pharmacology Neuroscience Nursing Physics Public Health Social Sciences Veterinary Other

Published : 112 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 112 Documents
Search

 1   2   3   4   5 
PENGARUH PENAMBAHAN BKT PADA PIEZOELEKTRIK RAMAH LINGKUNGAN BI0,5NA0,5TIO3-BATIO3-BI0,5K0,5TIO3 (BNT-BT-BKT) Mahyudin, Alimin
Jurnal Ilmu Fisika Vol 3, No 1 (2011): JURNAL ILMU FISIKA
Publisher : Jurnal Ilmu Fisika

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (383.552 KB) | DOI: 10.25077/jif.3.1.10-15.2011

Abstract

Proses sintesis BNT-BT-BKT telah dilakukan dengan menggunakan metode solid state reaction. Sintesis BNT-BT dengan penambahan % mol BKT yaitu 2%, 5%, 8%, 15% juga mendapatkan struktur perovskite dengan komposisi yang optimal pada penambahan 5% mol BKT. Pola difraksi XRD pada bahan BNT-BT dengan penambahan % mol BKT menunjukkan adanya perubahan puncak-puncak yang tumpang tindih dari (200) rhombohedral menjadi (200) dan (002) dari tetragonal. Daerah perubahan fasa ini dikenal dengan MPB yang terjadi pada komposisi penambahan BKT 2%. Penambahan bahan dopan BKT ke BNT-BT menunjukkan perubahan pola difraksi sinar-x dengan pergeseran sudut 45° - 47°. Mikrograph SEM, menunjukkan penambahan 2% BKT pada BNT-BT memiliki bentuk partikel seperti jarum dengan panjang rata-rata 1,608 – 2,589 μm.
Analisis Keluaran Berkas Radiasi Sinar-X Pesawat Terapi LINAC Berdasarkan TRS 398 IAEA Pada Fantom Air Di Instalasi Radioterapi RS Universitas Andalas Milvita, Dian; Mahyudin, Alimin; Vadila, Mona
Jurnal Ilmu Fisika Vol 10, No 2 (2018): Published in September 2018
Publisher : Universitas Andalas

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (533.1 KB) | DOI: 10.25077/jif.10.2.83-88.2018

Abstract

Telah dilakukan penelitian tentang analisis keluaran berkas sinar-X pesawat terapi linear acceleration (LINAC) pada fantom air.  Analisis ini bertujuan untuk mengetahui kondisi pesawat terapi LINAC selama digunakan dengan mengacu pada nilai 1 cGy sama dengan 1 MU.  Penelitian dilakukan dengan cara menganalisis muatan yang ditangkap oleh detektor ionisasi chamber dengan faktor koreksi suhu, tekanan, efek polaritas dan rekombinasi ion.  Penelitian dilakukan dengan variasi energi 6 MV dan 10 MV dengan ukuran luas lapangan penyinaran (10 x 10) cm dan teknik penyinaran Source to Surface Distance (SSD) 100 cm. Hasil analisis menunjukkan bahwa pada berkas sinar-X energi 6 MV dan 10 MV didapatkan nilai keluaran per 1 MU sebesar 1,026 cGy dan 1,025 cGy dengan deviasi pengukuran 2,60 % dan 2,56 %, nilai ini masih berada dalam rentang toleransi pengukuran yaitu ± 3 %.  Dengan demikian, keluaran berkas radiasi sinar-X pesawat terapi LINAC di Rumah Sakit Universitas Andalas (RS Unand) telah sesuai standar TRS 398 IAEA.Kata kunci: berkas sinar-X, fantom air, LINAC, RS Unand
Optimalisasi Persentase Serat Bambu Terhadap Sifat Fisis Papan Komposit Beton Ringan Mahyudin, Alimin; Yunita, Devi; Milvita, Dian
Jurnal Ilmu Fisika Vol 10, No 1 (2018): Published in March 2018
Publisher : Universitas Andalas

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.25077/jif.10.1.11-16.2018

Abstract

Telah dilakukan penelitian dengan judul optimalisasi serat bambu terhadap sifat fisis papan komposit beton ringan. Penelitian ini bertujuan untuk mengetahui pengaruh serat bambu terhadap sifat fisis papan komposit yang diharapkan dapat menghasilkan papan komposit beton ringan lebih kuat, lentur, ringan  dengan persentase serat bambu yang optimum. Penelitian dilakukan dengan menggunakan metode two dimensional reinforcement (planar) dalam penyusunan serat bambu. Persentase serat yang digunakan pada masing-masing sampel, yaitu 0%; 0,6%; 1,2%;2,5% dan 5% serta foam agent 0,06%, dan tebal sampel papan 1 cm.  Berdasarkan hasil pengujian nilai densitas optimum diperoleh  sebesar 1,63 g/cm3 pada serat 0,6% dari volume sampel,  kuat lentur optimum terdapat pada serat 0,6% dari volume sampel bernilai 44,25 kg/cm2 sedangkan nilai kuat tekan optimum diperoleh sebesar 6,9 kg/cm2 pada serat 2,5% dari volume sampel. Nilai kuat lentur  telah memenuhi standar  SNI 03-2104Kata kunci: Papan komposit, serat bambu, foam agent.
APLIKASI METODE MOLTEN SALT UNTUK SINTESIS BAHAN PIEZOELEKTRIK Bi0,5(Na0,5K0,5)0,5TiO33 Syahfandi Ahda; Mardiyanto Mardiyanto; Alimin Mahyudin
Jurnal Sains Materi Indonesia Vol 14, No 4: JULI 2013
Publisher : Center for Science & Technology of Advanced Materials - National Nuclear Energy Agency

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (275.77 KB) | DOI: 10.17146/jsmi.2013.14.4.4387

Abstract

APLIKASI METODE MOLTEN SALT UNTUK SINTESIS BAHAN PIEZOELEKTRIK Bi0,5(Na0,5K0,5)0,5TiO3. Telah dikembangkan sintesis bahan piezo elektrik ramah lingkungan (bebas Pb) dengan menggunakan metode molten salt untuk bahan piezoelektrik Bi0,5(Na0,5K0,5)0,5TiO3 (BNKT). Sintesis BNKT dilakukan dalam lingkungan lelehan garam NaCl dan KCl pada suhu sintering 950 oC. Bahan-bahan dasar Bi2O3, Na2CO3, K2CO3 memiliki suhu leleh dibawah suhu lelehan garam, sedangkan TiO32 berada diatas suhu sintering. BNKT diperoleh dalam dua tahap yakni terlebih dahulu mensintesis Bi2Ti4O12 (BIT) kemudian dilanjutkan dengan sintesis BNKT. Pada proses sintesis dengan metode molten salt ini terjadi reaksi difusi bahan-bahan dasar (lelehan) ke partikel bahan dasar TiO32 membentuk produk baru BIT maupun BNKT. Pada penelitian ini juga dilakukan sintesis BNKT dari BIT menggunakan metode solid state reacTiO3n sebagai pembanding. Dari hasil karakterisasi fasa dan strukturmikro bahan BNKT masing-masing dengan metode difraksi sinar-X dan Scanning Electron Microscope (SEM), diperoleh bahwa dengan metode molten salt transformasi bahan dasar menjadi produk baru BNKT lebih baik dibandingkan dengan metode solid state reaction.
Pengaruh Persentase Massa Gipsum Dan Serat Terhadap Kuat Tekan Dan Kuat Lentur Papan Semen - Gipsum Berserat Enceng Gondok Ummi Qorina; Alimin Mahyudin; Sri Handani
Jurnal Fisika Unand Vol 5 No 3 (2016)
Publisher : Universitas Andalas

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (57.364 KB) | DOI: 10.25077/jfu.5.3.233-237.2016

Abstract

Telah dilakukan penelitian tentang pengaruh persentase massa gipsum dan serat terhadap kuat tekan dan kuat lentur papan semen-gipsum berserat eceng gondok. Alat uji Kuat tekan dan kuat lentur  diukur menggunakan universal testing machine (UTM). Dari hasil pengujian terhadap papan semen-gipsum dengan persentase massa serat tetap 2,5% diperoleh nilai kuat tekan paling tinggi yaitu sebesar 14,52 kg/cm2 pada persentase massa gipsum 30%. Sedangkan pada papan semen-gipsum dengan persentase massa gipsum tetap 30% diperoleh nilai  kuat tekan tertinggi sebesar 24,99 kg/cm2 pada persentase massa serat 7,5%. Hasil pengujian terhadap papan semen-gipsum dengan persentase massa serat tetap 2,5% diperoleh nilai kuat lentur paling tinggi yaitu sebesar 1,265 kg/cm2 pada persentase massa gipsum 30%. Sedangkan pada papan semen-gipsum dengan persentase massa gipsum tetap 30% diperoleh nilai  lentur tertinggi sebesar 1,575 kg/cm2 pada persentase massa serat 5%.Kata kunci: papan semen-gipsum, serat eceng gondok, kuat tekan dan kuat lentur.
Analisis Pengaruh Komposisi Serat Pinang dan Serat Eceng Gondok terhadap Sifat Mekanik Komposit Hibrid Polipropilena dengan Pati Talas Yuliana Yoniza; Alimin Mahyudin
Jurnal Fisika Unand Vol 9 No 1 (2020)
Publisher : Universitas Andalas

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (359.695 KB) | DOI: 10.25077/jfu.9.1.24-30.2020

Abstract

Telah dilakukan penelitian tentang pengaruh komposisi serat pinang dan eceng gondok terhadap sifat mekanik komposit hibrid polipropilena dengan pati talas. Komposisi serat pinang dan eceng gondok divariasikan dengan perbandingan persen volume yaitu 1,25%: 3,75%, 2,5%: 2,5%, 3,75%: 1,25% dengan panjang serat 3 mm. Sifat mekanik yang diujikan meliputi kuat tarik, regangan, modulus elastisitas, kuat impak dan uji biodegradabel. Sifat fisika yang diuji yaitu morfologi permukaan dengan menggunakan SEM. Berdasarkan hasil pengujian didapatkan nilai kuat tarik tertinggipada perbandingan 1,25%: 3,75% yaitu 14,33 MPa. Nilai kuat impak tertinggi ditemukan pada sampel dengan perbandingan 2,5%: 2,5% yaitu 0,041 J/mm2. Nilai regangan tertinggi didapatkan pada perbandingan 3,75%: 1,25% sebesar 1,27%. Pada uji biodegradabel didapatkan hasil sebesar 0,021%/hari. Pada penelitian ini masih terdapat rongga dan juga pati talas dan polipropilenanya tidak tercampur sempurna karena masih ditemukan gumpalan-gumpalan pati talas. Hal ini didapatkan dari hasil analisis morfologi struktur patahan uji tarik menggunakan SEM. A Research on the effect of areca nut and water hyacinth composition on the mechanical properties of polypropylene hybrid composites with taro starch has been conducted. The composition of areca nut and water hyacinth fiber is varied with a volume percent ratio of 1.25%: 3.75%, 2.5%: 2.5%, 3.75%: 1.25% with a fiber length of 3 mm. Mechanical properties tested include tensile strength, stretch, modulus of elasticity, impact strength and biodegradable test. Physical properties tested were surface morphology using SEM. Based on the test results obtained the highest value of tensile strength at a ratio of 1.25%: 3.75% ie 14.33 MPa. The highest impact strength value was found in samples with a ratio of 2.5%: 2.5% ie 0.041 J/mm2.  The highest strain value obtained at a ratio of 3.75%: 1.25% of 1.27%. In the biodegradable test results obtained by 0.021%/days. In this researchthere were still voids, taro starch and polypropylene in the samples was not completely mixed because there were still lumps of taro starch. This was obtained from the morphological analysis of the tensile test fault structure using SEM. The impact strength value of this research meets the car dashboard standards.
PENGARUH PENAMBAHAN SERAT PINANG (Areca catechu L. Fiber) TERHADAP SIFAT MEKANIK DAN SIFAT FISIS BAHAN CAMPURAN SEMEN GIPSUM Suci Olanda; Alimin Mahyudin
Jurnal Fisika Unand Vol 2 No 2: April 2013
Publisher : Universitas Andalas

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (401.09 KB) | DOI: 10.25077/jfu.2.2.%p.2013

Abstract

Telah dilakukan penelitian tentang sifat mekanik dan sifat fisis papan semen gipsum dengan penambahan serat pinang.  Metode penyusunan serat pinang yang digunakan yaitu 1 lapis secara teratur yang diletakkan diantara matriks, dengan variasi persentase serat yang digunakan adalah 0%, 0,2%, 0,4%, 0,6%,08% dan 1,2% terhadap massa adonan serat, semen, gipsum dan air.  Dari hasil pengujian didapatkan nilai optimum kuat tekan diperoleh pada papan dengan persentase serat 0,6% yaitu sebesar 108,08 kg/cm2, sedangkan nilai kuat lentur optimum diperoleh pada papan dengan persentase serat 0,6% yaitu sebesar 30,33 kg/cm2.  Daya serap air optimum diperoleh persentase serat 1,2% yakni sebesar 16,52%, sedangkan densitas optimum diperoleh pada persentase serat 0,8% yaitu sebesar 1,139 g/cm3.  Nilai kuat tekan dan densitas memenuhi standar JIS A 5908-2003 dan SNI 03-6384-2000, sedangkan nilai kuat lentur telah memenuhi standar bison gypsum fiber board  dan daya serap air memenuhi standar FAO.
Analisis Pengaruh Komposisi Serat Pinang dan Sabut Kelapa Terhadap Sifat Fisis Papan Beton Ringan Dengan Agregat Halus Sekam Padi Habib Andrestama; Alimin Mahyudin
Jurnal Fisika Unand Vol 10 No 3 (2021)
Publisher : Universitas Andalas

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (760.889 KB) | DOI: 10.25077/jfu.10.3.405-412.2021

Abstract

Telah dilakukan peneltian tentang analisis pengaruh komposisi serat pinang dan sabut kelapa terhadap sifat fisis papan beton ringan dengan agregat halus sekam padi. Penelitian ini bertujuan untuk mengetahui pengaruh komposisi dari serat pinang dan serat sabut kelapa terhadap sifat fisis papan beton ringan dengan agregat halus sekam padi. Perbandingan persentase serat pinang dan serat sabut kelapa yang digunakan berturut – turut adalah 0,4 % : 1,6 % ; 0,8 % : 1,2 % ; 1 % :1 % ; 1,2 % : 0,8 % ; 1,6 % : 0,4 %. Pengujian yang dilakukan pada sampel yaitu uji sifat fisik (densitas dan porositas) dan uji sifat mekanik (kuat tekan dan kuat lentur). Nilai densitas minimum diperoleh sebesar 1,33 g/cm3 pada sampel A5, dan sudah memenuhi standar SNI 03-3449-2002. Sedangkan nilai porositas minimum diperoleh pada sampel A5 sebesar 28,59 %. Nilai kuat tekan maksimum yang diperoleh yaitu pada sampel A1 sebesar 50,87 kg/cm2. Untuk nilai kuat lentur maksimum yang diperoleh yaitu pada sampel B5 yitu sebesar 48 kg/cm2. Dari beberapa variabel yang diuji hanya nilai densitas yang sudah memenuhi standar SNI 03-3449-2002. Nilai porositas, kuat tekan dan kuat lentur masih belum memenuhi standar SNI 03-2015-2006.
PENGARUH PENAMBAHAN BAHAN DOPAN TA2O5 PADA BAHAN PIEZOELEKTRIK RAMAH LINGKUNGAN (K0,5NA0,5)0,96LI0,04NO3 DENGAN MENGGUNAKAN SINTESIS METODE MOLTEN SALT Awaluddin -; Alimin Mahyudin; Syahfandi Ahda
Jurnal Fisika Unand Vol 4 No 2: April 2015
Publisher : Universitas Andalas

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (263.244 KB) | DOI: 10.25077/jfu.4.2.%p.2015

Abstract

ABSTRAKTelah dilakukan penelitian tentang pengaruh penambahan bahan dopan Ta2O5 pada bahan piezoelektrik ramah lingkungan (K0,5Na0,5)0,96Li0,04NbO3(KNLN)dengan metode sintesis  molten salt.  Dalam penelitian ini  dilakukan variasi persentase mol bahan dopan Ta2O5  sebesar 3%, 7%, 10% dan 12%. Sintesis dilakukan dengan parameter penggerusan selama 4 jam, kalsinasi pada suhu 2500C selama 1 jam, dan sintering pada suhu 9200C selama 4 jam. Berdasarkan analisis XRD dapat diidentifikasi bahwa struktur bahan piezoelektrik KNLNT (KNLN + dopan) pada penambahan 3% dan 7% cenderung ortorhombik, sedangkan pada penambahan 10% dan 12% cenderung tetragonal. Pada penambahan 7% mol Ta2O5 terjadinya penurunan nilai c/a yang tajam. Hal ini menunjukkan bahwa pada rentang komposisi inilah daerah motphotropic phase boundary berada.  Hasil SEM menunjukkan pada penambahan dopan 3% ukuran partikel adalah 0,0884-0,7869 μm dan penambahan dopan 12% terjadi lonjakan tajam ukuran partikel yaitu sebesar 0,1563-1,5793 μm.AbstractResearch on the effect of the addition of dopant materials Ta2O5 on environmentally friendly piezoelectric materials (K0,5Na0,5)0,96Li0,04NbO3(KNLN) with molten salt synthesis method has been conducted. In this study, the mole percentage dopant materials varied by 3%, 7%, 10% and 12%. Synthesis was conducted with parameters: grinding for 4 hours, temperature calcination at 2500Cfor 1 hour, and sintering at a temperature of 9200C for 4 hours. Based on XRD analysis, it can be identified that the structure of the piezoelectric material KNLNT (KNLN + dopant) on the addition of 3% and 7% tend orthorhombic, while the addition of 10% and 12% tend to tetragonal. In addition of 7 % mol of Ta2O5, the c/a value decrese sharply. This value indicates that motphotropic phase boundary is located in this composition range. The SEM results show that at addition of 3% dopants the particle size is from 0.0884 to 0.7869 μm and at addition of 12% dopant the particle size increase sharply that  to 0.15623 until 1.5793 μm. 
Analisis Sifat Fisis dan Mekanik Papan Komposit Gipsum Serat Ijuk dengan Penambahan Boraks (Dinatrium Tetraborat Decahydrate) Hilda Trisna; Alimin Mahyudin
Jurnal Fisika Unand Vol 1 No 1: Oktober 2012
Publisher : Universitas Andalas

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (264.871 KB) | DOI: 10.25077/jfu.1.1.%p.2012

Abstract

Penelitian mengenai sifat fisis dan mekanik papan gipsum dengan penambahan serat ijuk (arrenge pinnata) dan boraks (dinatrium tetraborat decahydrate) telah dilakukan.  Metode penyusunan serat yang digunakan yaitu 1 lapis secara teratur yang diletakkan di antara matriks, dengan variasi persentase serat 0,5%, 1,0%, 1,5%, 2,0%, dan 2,5% terhadap massa tepung gipsum, sedangkan kadar boraks yang digunakan yaitu 0,5% terhadap massa total adonan.  Dari hasil pengujian diperoleh, nilai optimum daya serap air diperoleh pada papan dengan persentase serat 2,5% yaitu sebesar 24,32%, sedangkan nilai densitas optimum diperoleh pada papan dengan persentase serat 1,0% yaitu sebesar 1,4 g/cm3.  Kuat tekan optimum diperoleh pada papan dengan persentase serat 1,0%, yakni sebesar 133,95 kg/cm2, sedangkan nilai kuat lentur optimum terdapat pada papan dengan persentase serat 2,0% yaitu 45,38 kg/cm2.  Nilai daya serap air dan kuat tekan telah memenuhi standar mutu papan, sedangkan densitas dan kuat lentur belum memenuhi standar.
Co-Authors A. Fadhil Desafa Adrial, Rico Afdal Afdal Afdal Afdal Afdhal Muttaqin Agus Taufiq Ahmad Fauzi Pohan Al Rahman Annisa, Hafizha Fitri Arif Budiman Arif Budiman Arsal Chayri Iby Astuti Astuti Astuti - Awaluddin - Ayuzia Puspa Indah Betta Centaury Dahyunir Dahlan Damayanti, Elok Dedi Mardiansyah Defta Eka Sari Della Amelia Deora Murza Oktora Deri Wahyuni Devi Yunita Devi Yunita Devi Yunita Dian Fitriyani Dian Fitriyani Dian Milvita Dwi Pujiastuti Dwi Pujiastuti Dwi Puryanti Elistia Liza Namigo, Elistia Elvaswer Engkir Sukirman Fajar Anugrah Fani Anjelina Feriska Handayani Feriska Handayani Irka, Feriska Handayani Fiqi Diyona Firda Yulia Citra Geby Sri Ayu Oktavia Habib Andrestama Hafiza Rahmi Zul Afri Haldis Alvaro Hana Aulia Hanifah Karmuliani Harmadi Harmadi Harmadi Harmadi Hilda Trisna Husna Dhia Imam Taufiq Imam Taufiq Indah Pratiwi Desha Putri Ira Febri Winda Kgs Haprido Lara Putri Jatmika Lovely Dwina Putri M. Ali Shafii M. Wahyu Ramadhani Mardiyanto - Mardiyanto Mardiyanto Mardiyanto Mardiyanto Marzuki Marzuki Mega Dwisa Meqorry Yusfi Meri Darmawi Meri Darmawi Mila Putri Artika Mohammad Ali Shafii Mona Vadila Muhammad Blestynsky Renaldi Muhammad Fachrul Rozi Muldarisnur, Mulda Mutia Sukma Dewi Mutya Vonnisa Nini Firmawati Nur 'Arifah Nurul Annisa Nurul Hasanah Nurul Nabila Olly Norita Tetra Paridah Anum Rahmat Rasyid Ramacos Fardela Randa Randa Rasyid Ridho Ressi Anggraini Riefli Fatmi Salim Muhaimin Shelly Monica Sindy Dwi Putri Dynanty Solly Aryza Sonia Yong Lisha Sri Handani Sri Oktamuliani Suci Olanda Syahfandi Ahda Syahfandi Ahda Syahfandi Ahda Syahfandi Ahda Trengginas Eka Putra Trengginas Eka Putra Sutantyo Uchi Delfia Ummi Qorina Ummi Qorina Usna, Sri Rahayu Alfitri Vadila, Mona Vinny Alvionita Wildian Wildian Yanandra Amelia Putri Yazid Reza Hanovatias Yosi Sylvia Yuliana Yoniza Yusfi, Meqqory Zozy Aneloi Noli Zulfi Zulfi Zulfi Zulfi Zulfi Zulfi Zulfi, Zulfi